Material: | POF |
---|---|
Usage: | Packaging Film, Food&Medicine Film |
Type: | Shrink Film |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Item# | Pack Type | Measurement(Roll) | |||||
(Thickness) um * (Length) m | |||||||
SWD-01 | standard(corner folded) | 12*1667 | 15*1332 | 19*1067 | 25*800 | 30^666 | 38*560 |
SWD-01R | Hot Slip(corner folded) | 12*1667 | 15*1332 | 19*1067 | 25*800 | 30*666 | 38*560 |
SWD-01G | High-speed(single wound) | 19*3000 | 22*2500 | 25*2130 | |||
SWD-01W |
High-speed(single wound) | 10*3000 | 11*3000 | 12*3000 |
SWD-01 Polyolefin Shrink Film | ||||||||
TEST ITEM | UNIT | ASTMTEST | TYPICAL VALUES | |||||
THICKNESS | 12um | 15um | 19um | 25um | 30um | |||
OPTICS | ||||||||
Haze | D1003 | 2.2 | 2.5 | 2.6 | 3.2 | 4 | ||
Clarity | D1746 | 98.5 | 98.5 | 98 | 97 | 92 | ||
Gloss @45Deg | D2457 | 85.5 | 85.5 | 87 | 83.5 | 80 | ||
BARRIER | ||||||||
Oxygen Transmission Rate | cc/m²/day | D3985 | 11300 | 11000 | 10800 | 7200 | 7000 | |
Water Vapor Transmission Rate | gm/m²/day | F1249 | 41.5 | 45.5 | 38.5 | 26.5 | 20.5 | |
SHRINKAGE PROPERTIES | MD | TD | MD | TD | TD | |||
Free Shrinkage | 100ºC | % | D2732 | 30 | 32 | 20 | 26 | 26 |
110ºC | 45 | 45 | 35 | 43 | 43 | |||
120ºC | 63 | 62 | 57 | 60 | 60 | |||
130ºC | 66 | 68 | 65 | 65 | 65 | |||
Shrink Tension | 100ºC | Mpa | 2.65 | 2.6 | 1.8 | 2.6 | 2.6 | |
110ºC | 3.55 | 3.39 | 2.75 | 3.43 | 3.43 | |||
120ºC | 3.6 | 3.5 | 2.85 | 3.65 | 3.65 | |||
130ºC | D2838 | 3.16 | 3.25 | 2.85 | 3.4 | 3.4 | ||
TENSILE | ||||||||
Tensile Strength(MD) | N/mm² | D882 | 115 | 110 | 105 | 95 | 95 | |
Tensile Strength(TD) | 110 | 105 | 100 | 90 | 90 | |||
Elongation(MD) | % | 115 | 116 | 120 | 126 | 126 | ||
Elongation(TD) | 110 | 110 | 116 | 123 | 123 | |||
TEAR | ||||||||
MD | g | D1922 | 10.5 | 10.5 | 14.5 | 17.5 | 19 | |
TD | 10 | 10 | 13.5 | 16 | 18 | |||
SEAL STRENGTH | ||||||||
MD/Hot Wire Seal | N/mm | F88 | 0.65 | 0.65 | 0.81 | 1.03 | 1.2 | |
TD/Hot Wire Seal | 0.68 | 0.68 | 0.86 | 1.06 | 1.1 | |||
COF(Film To Film) | ||||||||
Dynamic | D1894 | 0.23 | 0.23 | 0.22 | 0.22 | 0.22 | ||
Static | 0.24 | 0.24 | 0.23 | 0.24 | 0.24 |
SWD-06 Cross-linked Polyolefin Shrink Film | ||||||||
TEST ITEM | UNIT | ASTMTEST | TYPICAL VALUES | |||||
THICKNESS | 12um | 15um | 19um | 25um | 30um | |||
OPTICS | ||||||||
Haze | D1003 | 2.3 | 2.5 | 3.5 | 3.7 | 4.2 | ||
Clarity | D1746 | 98.5 | 98.5 | 98 | 97.5 | 94.5 | ||
Gloss @45Deg | D2457 | 88.5 | 88 | 87 | 86 | 86 | ||
BARRIER | ||||||||
Oxygen Transmission Rate | cc/m²/day | D3985 | 10250 | 9600 | 6200 | 5500 | 4250 | |
Water Vapor Transmission Rate | gm/m²/day | F1249 | 34.5 | 29 | 22 | 15 | 11 | |
SHRINKAGE PROPERTIES | MD | TD | ||||||
Free Shrinkage | 100ºC | % | D2732 | 28 | 37 | |||
110ºC | 52 | 57 | ||||||
120ºC | 75 | 76 | ||||||
130ºC | 78 | 79 | ||||||
Shrink Tension | 100ºC | Mpa | 2.1 | 2.6 | ||||
110ºC | 2.7 | 3.8 | ||||||
120ºC | 2.9 | 4.2 | ||||||
130ºC | D2838 | 2.8 | 4 | |||||
TENSILE | ||||||||
Tensile Strength(MD) | N/mm² | D882 | 131 | 135 | 135 | 135 | 135 | |
Tensile Strength(TD) | 125 | 125 | 124 | 130 | 129 | |||
Elongation(MD) | % | 126 | 130 | 125 | 130 | 130 | ||
Elongation(TD) | 122 | 125 | 120 | 131 | 135 | |||
TEAR | ||||||||
MD | g | D1922 | 10.2 | 14.8 | 20 | 25.6 | 34 | |
TD | 9.6 | 13.5 | 17 | 25.5 | 30.5 | |||
SEAL STRENGTH | ||||||||
MD/Hot Wire Seal | N/mm | F88 | 1.15 | 1.39 | 1.5 | 1.77 | 2.15 | |
TD/Hot Wire Seal | 1.18 | 1.43 | 1.69 | 1.76 | 2.12 | |||
COF(Film To Film) | ||||||||
Dynamic | D1894 | 0.25 | 0.22 | 0.23 | 0.25 | 0.26 | ||
Static | 0.23 | 0.21 | 0.22 | 0.25 | 0.25 |
SWD-09 Oxo-biodegradable Polyolefin Shrink Film | ||||||||
TEST ITEM | UNIT | ASTMTEST | TYPICAL VALUES | |||||
THICKNESS | 10um | 15um | 19um | 25um | 30um | |||
OPTICS | ||||||||
Haze | D1003 | 2.2 | 2.6 | 3.2 | 3.9 | 4.0 | ||
Clarity | D1746 | 98.5 | 98 | 97 | 95 | 92 | ||
Gloss @45Deg | D2457 | 86 | 87.5 | 84.5 | 82.2 | 81.5 | ||
BARRIER | ||||||||
Oxygen Transmission Rate | cc/m²/day | D3985 | 11350 | 10800 | 7250 | 5450 | 4500 | |
Water Vapor Transmission Rate | gm/m²/day | F1249 | 46.5 | 38.5 | 26 | 22.5 | 20.5 | |
SHRINKAGE PROPERTIES | MD | MD | ||||||
Free Shrinkage | 100ºC | % | D2732 | 23 | 20 | |||
110ºC | 38 | 35 | ||||||
120ºC | 59 | 58 | ||||||
130ºC | 66 | 65 | ||||||
Shrink Tension | 100ºC | Mpa | 1.85 | 1.86 | ||||
110ºC | 2.75 | 2.86 | ||||||
120ºC | 2.85 | 3.75 | ||||||
130ºC | D2838 | 2.65 | 3.25 | |||||
TENSILE | ||||||||
Tensile Strength(MD) | N/mm² | D882 | 113 | 117 | 118 | 119 | 120 | |
Tensile Strength(TD) | 113 | 116 | 117 | 118 | 119 | |||
Elongation(MD) | % | 115 | 121 | 122 | 125 | 126 | ||
Elongation(TD) | 109 | 115 | 117 | 118 | 120 | |||
TEAR | ||||||||
MD | g | D1922 | 10 | 15 | 18 | 23.5 | 28.5 | |
TD | 9.5 | 14.5 | 17.5 | 22.5 | 28 | |||
SEAL STRENGTH | ||||||||
MD/Hot Wire Seal | N/mm | F88 | 0.63 | 0.82 | 1.04 | 1.25 | 1.55 | |
TD/Hot Wire Seal | 0.65 | 0.87 | 1.06 | 1.32 | 1.75 | |||
COF(Film To Film) | ||||||||
Dynamic | D1894 | 0.25 | 0.23 | 0.23 | 0.25 | 0.25 | ||
Static | 0.23 | 0.22 | 0.22 | 0.24 | 0.25 |